It is a water-based epoxy dispersion, which is recommended to be used with a water-based epoxy curing agent to prepare high-performance water-based epoxy coatings. It is designed for anti- corrosion primers and epoxy floor paints for various metal substrates.
Features: Faster surface drying speed, suitable for various wet-on-wet matching processes, rapid hardness build-up, and long pot life period
Physical Property
| Appearance | Milky white liquid |
| Non-volatile matter (Wt, %) | 54±2 |
| Viscosity (mPa·s) (25℃) | 500 ~ 8000 |
| Epoxy equivalent (supplied form) (g/Eq) | 1060±50 |
layer is applied directly over the uncured base coat, resulting in a composite finish with zero blister formation).
The cured coating exhibits exceptional gloss retention (>92° at 60° measurement, per ASTM D523),
demonstrating superior surface quality even under multi-layer application conditions.
Key Technical Enhancements:
Process compatibility: Explicitly defines wet-on-wet workflow with performance validation
Blister resistance: Uses "zero blister formation" to align with NACE TM0177 standards
Gloss measurement: Specifies angle of measurement (60°) per ISO 2813
Process efficiency: Implies reduced energy consumption through elimination of intermediate drying stages
Layer integrity: "Composite finish" emphasizes adhesion performance between layers
Product Tags:
|
|
Faster Surface Drying Water Borne Epoxy Resin Liquid For Wet On Wet Application Images
|